Spezifikation:
Dicke (mm) | Breite (mm) | Länge (mm) | |
vereiteln | 0,03-0.09 | 30-150 | ﹤2000 |
Billet | 0,1-0,5 | 30-600 | 30-2000 |
Blech | 0,5-10 | 50-1000 | 50-2000 |
Zusammensetzungstabelle:
Komposition,％ | |||||||||||||
Material | Hauptkomposition | Verunreinigungen Maxmium | |||||||||||
Ta | NB | Fe | Si | Ni | W | MO | Ti | NB | O | C | H | N | |
Ta1 | Überschuss | ——— | 0.005 | 0.005 | 0.002 | 0.01 | 0.01 | 0.002 | 0.03 | 0.015 | 0.01 | 0.0015 | 0.01 |
Ta2 | Überschuss | ——— | 0.03 | 0.02 | 0.005 | 0.04 | 0.03 | 0.005 | 0.1 | 0.02 | 0.01 | 0.0015 | 0.01 |
Tanb3 | Überschuss | ＜3.5 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | ——— | 0.02 | 0.01 | 0.0015 | 0.01 |
Tanb20 | Überschuss | 17.0～23.0 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | ——— | 0.02 | 0.01 | 0.0015 | 0.01 |
Ta2.5W | Überschuss | 0.005 | 0.005 | 0.002 | 3.0 | 0.01 | 0.002 | 0.04 | 0.015 | 0.01 | 0.0015 | 0.01 | |
TA10W | Überschuss | 0.005 | 0.005 | 0.002 | 11 | 0.01 | 0.002 | 0.04 | 0.015 | 0.01 | 0.0015 | 0.01 | |
Wenn Benutzer spezielle Anforderungen haben, können wir diskutieren. | |||||||||||||
Mechanische Eigenschaften:
Spezifikation und Form
| Getemperter Staat | ||
Ultimate Zugfestigkeit, min., Pfund/in.2（MPA） | Ertragsfestigkeit min., Pfund/Zoll 2 （MPA） （2％remanente Stamm） | Eogation，Mindest％ （1 Zoll Messlänge） | |
Mittelplatte、Lamina und Folie (RO5200， RO5400) Dicke <0,060 "(1,524 mm) Dicke ≥ 0,060 "(1,524 mm) | 30000 (207) | 20000 (138) | 20 |
25000 (172) |
15000 (103) | 30 | |
Tantalum 10 Wolfram (RO5255) Mittelplatte、Lamina und Folie | 70000 (482) | 60000 (414) | 15 |
70000 (482) |
55000 (379) | 20 | |
Tantalum 2,5 Wolfram (RO5252) Dicke <0,125 "(3,175 mm) Dicke ≥ 0,125 "(3,175 mm) |
40000 (276) |
30000 (207) | 20 |
40000 (276) |
22000 (152) | 25 | |
Tantal Tungsten 40 (RO5240) Dicke <0,060 "(1,524 mm) Dicke ≥ 0,060 "(1,524 mm) |
35000 (241) |
20000 (138) | 25 |
35000 (241) |
15000 (103) | 25 | |
Spezifikation:
Dicke (mm) | Breite (mm) | Länge (mm) | |
vereiteln | 0,03-0.09 | 30-150 | ﹤2000 |
Billet | 0,1-0,5 | 30-600 | 30-2000 |
Blech | 0,5-10 | 50-1000 | 50-2000 |
Zusammensetzungstabelle:
Komposition,％ | |||||||||||||
Material | Hauptkomposition | Verunreinigungen Maxmium | |||||||||||
Ta | NB | Fe | Si | Ni | W | MO | Ti | NB | O | C | H | N | |
Ta1 | Überschuss | ——— | 0.005 | 0.005 | 0.002 | 0.01 | 0.01 | 0.002 | 0.03 | 0.015 | 0.01 | 0.0015 | 0.01 |
Ta2 | Überschuss | ——— | 0.03 | 0.02 | 0.005 | 0.04 | 0.03 | 0.005 | 0.1 | 0.02 | 0.01 | 0.0015 | 0.01 |
Tanb3 | Überschuss | ＜3.5 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | ——— | 0.02 | 0.01 | 0.0015 | 0.01 |
Tanb20 | Überschuss | 17.0～23.0 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | ——— | 0.02 | 0.01 | 0.0015 | 0.01 |
Ta2.5W | Überschuss | 0.005 | 0.005 | 0.002 | 3.0 | 0.01 | 0.002 | 0.04 | 0.015 | 0.01 | 0.0015 | 0.01 | |
TA10W | Überschuss | 0.005 | 0.005 | 0.002 | 11 | 0.01 | 0.002 | 0.04 | 0.015 | 0.01 | 0.0015 | 0.01 | |
Wenn Benutzer spezielle Anforderungen haben, können wir diskutieren. | |||||||||||||
Mechanische Eigenschaften:
Spezifikation und Form
| Getemperter Staat | ||
Ultimate Zugfestigkeit, min., Pfund/in.2（MPA） | Ertragsfestigkeit min., Pfund/Zoll 2 （MPA） （2％remanente Stamm） | Eogation，Mindest％ （1 Zoll Messlänge） | |
Mittelplatte、Lamina und Folie (RO5200， RO5400) Dicke <0,060 "(1,524 mm) Dicke ≥ 0,060 "(1,524 mm) | 30000 (207) | 20000 (138) | 20 |
25000 (172) |
15000 (103) | 30 | |
Tantalum 10 Wolfram (RO5255) Mittelplatte、Lamina und Folie | 70000 (482) | 60000 (414) | 15 |
70000 (482) |
55000 (379) | 20 | |
Tantalum 2,5 Wolfram (RO5252) Dicke <0,125 "(3,175 mm) Dicke ≥ 0,125 "(3,175 mm) |
40000 (276) |
30000 (207) | 20 |
40000 (276) |
22000 (152) | 25 | |
Tantal Tungsten 40 (RO5240) Dicke <0,060 "(1,524 mm) Dicke ≥ 0,060 "(1,524 mm) |
35000 (241) |
20000 (138) | 25 |
35000 (241) |
15000 (103) | 25 | |